Pengaruh Variasi Kuat Arus Pengelasan (SMAW) Terhadap Uji Bending Dan Struktur Mikro Pada Pipa Stainless Steel 316 ASTM A213

Arifin, Fahmi (2022) Pengaruh Variasi Kuat Arus Pengelasan (SMAW) Terhadap Uji Bending Dan Struktur Mikro Pada Pipa Stainless Steel 316 ASTM A213. Undergraduate thesis, Universitas Muhammadiyah Jember.

[img] Text
a. PENDAHULUAN.pdf

Download (3MB)
[img] Text
b. ABSTRAK.pdf

Download (390kB)
[img] Text
c. BAB 1.pdf

Download (1MB)
[img] Text
d. BAB II.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy
[img] Text
e. BAB III.pdf
Restricted to Repository staff only

Download (1MB) | Request a copy
[img] Text
f. BAB IV.pdf
Restricted to Repository staff only

Download (866kB) | Request a copy
[img] Text
g. BAB V.pdf
Restricted to Repository staff only

Download (392kB) | Request a copy
[img] Text
h. DAFTAR PUSTAKA.pdf

Download (222kB)
[img] Text
i. LAMPIRAN.pdf
Restricted to Repository staff only

Download (5MB) | Request a copy
[img] Text
j. JURNAL.pdf

Download (1MB)

Abstract

Pengertian SMAW (Shield Metal Arc Welding) adalah las busur listrik nyala. Proses las SMAW terdiri dari pembungkus elektroda, sumbu kawat, daerah sekitar busur (arc), gas perisai, logam yang di endapkan dan terak (slag) yang telah mengeras. Mesin las SMAW menurut arusnya dibedakan menjadi tiga macam yaitu mesin las arus searah atau Direct Current (DC),mesin las arus bolak-balik atau Alternating Current (AC). Pada penelitian ini menggunakan bahan pipa stainless steel 316 dengan variasi arus pengelasan 70 Ampere, 80 Ampere dan 90 Ampere menggunkan kampuh I dan menggunakan pengujian bending dan struktur mikro. Berdasarkan data penelitian uji bending yang tertinggi yaitu pada arus pengelasan 80 A dengan defleksi 92,23 dan Mpa 20,136, sedangkan struktur mikro menggunakan metode point count tertinggi pada arus 80 A yaitu ferrite sebesar 27,6 dan pearlite sebesar 73,4. Sehingga disimpulkan bahwa arus pengelasan 80 A memenuhi standar KataKunci:LassSMAW,Stainless Steel,UjiBending

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: KataKunci:LassSMAW,Stainless Steel,UjiBending
Subjects: 600 Technology and Applied Science > 670 Manufacturing > 672 Iron and Steel Metalworking Process
Divisions: Faculty of Engineering > Department of Mechanical Engineering (S1)
Department: S1 Teknik Mesin
Depositing User: Fahmi Arifin
Contributors:
ContributionContributor NameNIDN/NIDK
Thesis advisorNusantara, Ardhi Fathonisyam PutraNIDN0728038002
Thesis advisorBahri, Mokh HairulNIDN0022047701
Contact Email Address: fahmiarifin058@gmail.com
Date Deposited: 14 Jan 2023 02:25
Last Modified: 14 Jan 2023 02:25
URI: http://repository.unmuhjember.ac.id/id/eprint/15961

Actions (login required)

View Item View Item